GI wires are used for applications that demand longevity. These are mild carbon or high carbon steel wires, which are coated with Zinc, so as to impart the wires with superior rust resistance properties.

The zinc-coated galvanized wires are highly resistant to moisture and mechanical damage and have a very bright and smooth surface finish. We manufacture GI wires using Hot-Dip and Electro-Galvanized technology to ensure durability and long-lasting resistance against corrosion.

Elemental Connectors offer Hot Dip GI wires of consistent mechanical properties, uniform zinc coating and bright surface finish.

• Diameter – 0.30 mm to 5.60 mm
• Standards – IS:280-2006; IS:398 / and as per customer requirements
• Zinc coating – 20 to 90Gsm/sq m
• Coil Weight – 25 – 250 kg (depending upon size)

• Diameter: 0.40mm to 0.90 mm
• Quality: Soft
• UTS: 300 to 500 MPA
• Elongation: 10% minimum
• Zinc coating: 20-40 GSM/sq.mt

Diameter – 0.47mm (25.5 SWG)
Quality: Soft
Resistance: 0.65 to 0.80 ohm/M
Uts: 40 kg/mm2 (minimum)
Elongation: 12% (minimum)
Zinc coating: 25 g (minimum)
Application: Used in the detonator industry

PVC Coated welded wire is a low carbon steel wire, with PVC or PE, PP coated on the surface. PVC-coated welded wire offers strong adhesion and corrosion resistance. Different colour available for customers’ choice is another benefit of PVC-coated wire.

Grades: Carbon contents vary from .06% to .018 %C, High carbon wire available upon request.
Finish: PVC.

Diameters – min 0.45mm to 4.5mm

Tensile (N/M2) – 350 -450

Material: Mild steel wire, PVC.
Application: PVC-coated wire finds popular applications as fencing, decoration or safety materials in industries, agriculture, construction, transport, etc.